Efecto de la nitruración por plasma a baja temperatura sobre la corrosión y las propiedades de la superficie del acero inoxidable dúplex UNS S32205
dc.contributor.author | Núñez de la Rosa, Yamid E. | |
dc.contributor.author | Palma Calabokis, Oriana | |
dc.contributor.author | Borges, Paulo César | |
dc.contributor.author | Ballesteros Ballesteros, Vladimir | |
dc.coverage.spatial | EEUU | spa |
dc.date.accessioned | 2021-05-20T19:58:24Z | |
dc.date.available | 2021-05-20T19:58:24Z | |
dc.date.issued | 2020 | |
dc.description.abstract | El acero inoxidable dúplex UNS S32205 se nitruró con plasma a 380 ° C durante 10 h usando una mezcla de gases de 25% N 2 -75% H 2 . El espesor de la capa nitrurada fue de 4,5 ± 0,5 µm, compuesta principalmente por precipitados de austenita expandida con nitrógeno y nitruros de hierro. Hubo un aumento en la dureza superficial alrededor de 2,6 y 3,8 veces en la capa nitrurada formada sobre las fases de austenita y ferrita, respectivamente, en relación con las muestras sin tratar. Los parámetros de textura de la superficie sesgo ( S sk ), altura máxima de pico ( S p ) y relación de aspecto de textura ( S tr) fueron los parámetros más adecuados para estudiar los cambios topográficos posteriores al tratamiento. Las curvas de polarización cíclica revelaron una mejora en las propiedades de corrosión localizada después del tratamiento de nitruración. Las muestras nitruradas mostraron un mayor potencial de corrosión por picadura y de repasivación en comparación con el material sin tratar. Las fases ferríticas y los límites de grano fueron más susceptibles a la corrosión en las muestras nitruradas. Las curvas potenciodinámicas de las muestras nitruradas exhibieron una ladera en la transición de pasivo a transpasivo. Esta característica ya fue observada por otros investigadores, pero no ha sido bien investigada. Los estudios potenciostáticos demostraron que se produjeron picaduras metaestables en esta transición. | spa |
dc.description.abstractenglish | The duplex stainless steel UNS S32205 was plasma nitrided at 380 °C for 10 h using a gas mixture of 25% N2-75% H2. The thickness of the nitrided layer was 4.5 ± 0.5 μm, composed mainly of nitrogen-expanded austenite and iron nitrides precipitates. There was an increase in surface hardness around 2.6 and 3.8 times in the nitrided layer formed on the austenite and the ferrite phases, respectively, in relation to the untreated samples. The surface texture parameters skewness (Ssk), maximum peak height (Sp) and texture aspect ratio (Str) were the most appropriate parameters for studying the topography changes after treatment. An improvement in the localized corrosion properties after the nitriding treatment was revealed by the cyclic polarization curves. The nitrided samples showed higher pitting corrosion and repassivation potentials compared to the untreated material. The ferritic phases and grain boundaries were more susceptible to corrosion in the nitrided samples. The potentiodynamic curves of the nitrided samples exhibited a hillside on the passive-to-transpassive transition. This feature was already observed by other researchers, but it has not been well investigated. Potentiostatic studies demonstrated that metastable pitting took place on this transition. | spa |
dc.description.publindex | Q2 | spa |
dc.description.researchgroup | Grupo de Investigación en Diseño, Análisis y Desarrollo de Sistemas de Ingeniería -GIDAD | spa |
dc.identifier.issn | 10599495 | |
dc.identifier.uri | http://hdl.handle.net/11371/3986 | |
dc.publisher.faculty | Facultad de Ingenieria y Ciencias Basicas | spa |
dc.relation.citationendpage | 11 | spa |
dc.relation.citationstartpage | 1 | spa |
dc.relation.citationvolume | 29 | spa |
dc.relation.ispartofjournal | Journal of Materials Engineering and Performance | spa |
dc.relation.uri | https://link.springer.com/article/10.1007%2Fs11665-020-04753-6 | spa |
dc.source.uri | https://www.springer.com/journal/11665 | spa |
dc.title | Efecto de la nitruración por plasma a baja temperatura sobre la corrosión y las propiedades de la superficie del acero inoxidable dúplex UNS S32205 | spa |
dc.title.translated | Effect of Low-Temperature Plasma Nitriding on Corrosion and Surface Properties of Duplex Stainless Steel UNS S32205 | spa |