Altas propiedades antibacterianas de la película DLC dopada con nanodiamante

Vista sencilla de ítem
dc.contributor.authorGutiérrez B, Jesus Manuel
dc.contributor.authorConceição, Katia
dc.contributor.authorAndrade, Vitor Martins
dc.contributor.authorTrava Airoldi, V.J.
dc.contributor.authorCapote, Gil
dc.coverage.spatialPaises Bajosspa
dc.date.accessioned2021-05-20T19:58:31Z
dc.date.available2021-05-20T19:58:31Z
dc.date.issued2019
dc.description.abstractLas películas DLC se utilizan en muchas aplicaciones y las nanopartículas se utilizan como materiales dopantes en una gran cantidad de películas. En esta investigación, las películas DLC dopadas con nanodiamante se depositaron sobre sustratos de Ti6Al4V. El nanodiamante de detonación (DND) se agitó en hexano con un sonicador a 750 W para obtener una suspensión, que se introdujo mediante un proceso de evaporación en un reactor PECVD para producir películas de DLC dopadas continuamente con nanopartículas. Se utilizó una capa intermedia de silicio amorfo antes de depositar el DLC sobre el sustrato Ti6Al4V. Los resultados de la espectroscopia Raman mostraron películas con un contenido de hidrógeno de alrededor del 22%. Una prueba de rayado en la aleación Ti6Al4V mostró cargas críticas cercanas a 19 N, y la resistencia a la corrosión medida mediante polarización potenciodinámica mejoró con DLC dopado sobre la del sustrato desnudo.Escherichia coli , mostrando actividad antibacteriana cercana al 95% 6 h después del contacto directo con la película. Este resultado sugirió que el DLC es un material excelente para fines biomédicos. Después de 18 h de contacto directo con la película de DLC dopada, se observó una actividad antibacteriana cercana al 25%, lo que sugirió que los nanodiamantes son capaces de mantener sus propiedades antibacterianas y producir daño a las células de E. colispa
dc.description.abstractenglishDLC films are used in many applications, and nanoparticles are being used as dopant materials in a large number of films. In this investigation, DLC films doped with nanodiamond were deposited on Ti6Al4V substrates. Detonation nanodiamond (DND) was stirred in hexane with a sonicator at 750 W to obtain a suspension, which was introduced by an evaporation process into a PECVD reactor to produce DLC films continuously doped with nanoparticles. An amorphous silicon interlayer was used before depositing the DLC on the Ti6Al4V substrate. Raman spectroscopy results showed films with hydrogen contents around 22%. A scratch test on the Ti6Al4V alloy showed critical loads close to 19 N, and corrosion resistance measured via potentiodynamic polarization was improved with doped DLC over that of the bare substrate. An antibacterial test was carried out with Gram-negative Escherichia coli, showing antibacterial activity close to 95% 6 h after direct contact with the film. This result suggested that DLC is an excellent material for biomedical purposes. After 18 h of direct contact with the doped DLC film, antibacterial activity close to 25% was observed, which suggested that nanodiamonds are able to maintain their antibacterial properties and produce damage to E. coli cells.spa
dc.description.publindexQ1spa
dc.description.researchgroupGrupo de Investigación en Diseño, Análisis y Desarrollo de Sistemas de Ingeniería -GIDADspa
dc.identifier.issn2578972
dc.identifier.urihttp://hdl.handle.net/11371/3997
dc.publisher.facultyFacultad de Ingenieria y Ciencias Basicasspa
dc.relation.citationendpage401spa
dc.relation.citationissue0spa
dc.relation.citationstartpage395spa
dc.relation.citationvolume375spa
dc.relation.ispartofjournalSurface '&' Coatings Technologyspa
dc.relation.urihttps://doi.org/10.1016/j.surfcoat.2019.07.029spa
dc.source.urihttps://www.sciencedirect.com/journal/surface-and-coatings-technologyspa
dc.titleAltas propiedades antibacterianas de la película DLC dopada con nanodiamantespa
dc.title.translatedHigh antibacterial properties of nanodiamond doped DLC filmspa